[Pellet Type] |
|
| Type |
Grade |
Chlorine content(%) |
Viscosity (mPa.s) |
Main uses |
| Chlorinated Polypropylene |
822S |
22.5 - 26.5 |
20 - 100 (1) |
Primer for PP,
Adhesives |
| 892LS |
20.0 - 24.0 |
20 - 100 (2) |
Primer for PP |
| 930S |
19.0 - 23.0 |
20 - 150 (2) |
Primer for PP |
| 803LS |
24.0 - 28.0 |
200 - 500 (3) |
Inks, Adhesives |
| 803MWS |
27.5 - 31.5 |
200 - 500 (3) |
Inks, Adhesives |
| 833S |
30.0 - 34.0 |
150 - 500 (4) |
Inks, Adhesives |
| 814HS |
39.0 - 43.0 |
500 - 2,000 (5) |
Inks |
| Chlorinated EVA |
BAS |
24.5 - 28.5 |
500 - 1,200 (3) |
Inks |
|
|
Viscosity is determined at 25 °C.
(1) 20% solid content toluene / IPA solution.
(2) 20% solid content toluene / cyclohexane / IPA solution.
(3) 20% solid content toluene solution.
(4) 30% solid content toluene solution.
(5) 60% solid content toluene solution.
These data are reported for information only, not for specification. |
|
[Non-toluene Solution Type] |
|
| Type |
Grade |
Chlorine content(%) |
Solid content (%)
|
Viscosity (mPa.s) |
Solvent |
Main uses |
| Chlorinated Polypropylene |
360T |
29.0 - 33.0 |
60 |
50 - 300 |
Ethyl Acetate |
Inks |
| 370M |
28.0 - 32.0 |
50 |
30 - 150 |
Ethyl Acetate/MCH = 1/1 |
Inks |
|
|
[Solution Type] |
|
| Type |
Grade |
Chlorine content(%) |
Solid content (%) |
Viscosity (mPa.s) |
Main uses |
| Chlorinated Polypropylene |
822 |
22.5 - 26.5 |
20 |
20 - 100 |
Primer for PP,
Adhesives |
| 892L |
20.0 - 24.0 |
20 |
20 - 100 |
Primer for PP |
| 842LM |
18.0 - 22.0 |
20 |
20 - 80 |
Primer for PP |
| 773H |
30.0 - 34.0 |
45 |
1,000 - 3,500 |
Coatings for PP |
| 832L |
25.0 - 29.0 |
30 |
20 - 100 |
Coatings for PP |
| 813A |
28.0 - 32.0 |
55 |
50 - 250 |
Inks |
| C |
33.0 - 37.0 |
55 |
500 - 2,000 |
Inks |
| Acrylic modified CPP |
223M |
3.0 - 7.0 |
35 |
500 - 1,000 |
Primer-less coatings for PP |
| 224H |
10.5 - 14.5 |
40 |
100 - 300 |
Primer-less coatings for PP |
| 240H |
2.5 - 6.5 |
30 |
500 - 2,500 |
Primer-less coatings for PP |
| Chlorinated PO |
S-309 |
20.0 - 24.0 |
20 |
200 - 500 |
Coatings for PE |
| Chlorinated EVA |
A |
9.5 - 13.5 |
20 |
200 - 500 |
Inks |
| B |
25.0 - 29.0 |
20 |
900 - 2,000 |
Inks |
| BX |
16.0 - 20.0 |
20 |
300 - 600 |
Inks |
|
|
Viscosity is determined at 25 .
These data are reported for information only, not for specification. |
|
|
|
|